H260BD+Z, H260BD+ZF Hot-dip galvanized steel

2014/5/6 2:08:32

H260BD+Z, H260BD+ZF Hot-dip galvanized steel

H260BD+Z, H260BD+ZF is under the standard Q/BQB 420-2003 and it is a kind of bake hardening of high strength steel, same as H180BD+Z, H180BD+ZF, H220BD+Z and H220BD+ZF steel. The products are widely used in the automotive, appliance, construction, machinery manufacturing and other industries.
H260BD+Z, H260BD+ZF Chemical composition:


Grade

Chemical composition %

C
max

Si
max

Mn
max

P
max

S
max

Alt
min

Tib
max

Nb
max

H260BD+Z, H260BD+ZF

0.08

0.5

0.7

0.1

0.025

0.02

-

-

H260BD+Z, H260BD+ZF Mechanical Property:


Grade

Tensile Strength
(Mpa)

Yield Strength
(Mpa)

n90

r90

BHb

Elongation% min

The coating adhesion
(The heart bending diameter ) a=thickness

min

min

Mpa

(Lo=80mm b=20mm)

<1.5

1.5-3.0

H260BD+Z, H260BD+ZF

360-440

260-320

-

-

30

28

2a

2a

a: For alloy hot dipped product, the elongation minimum value can reduce 2%, r90 can reduce 0.2.
b, BH value refers to puting the sample through 2% prestrain on the temperature 170C 土5C, keeping 20 minutes, then doing tensile test under the indoor temperature, the added value of measured yield strength compared with the stress at the time of the sample 2% prestrain.
c: When coating weight of the two sides is more than 180g/m2, the bending diameter adds to 1a; For difference thick coating products, thick coating surface as the outer surface of the bending test.

BEBON international is very professional in the production for that material and we have our own factory. We can supply it according to customer’s requirement.
If you have need for H260BD+Z, H260BD+ZF, please contact with us. Our email is [email protected] and our phone is 0086-371-86011527.

Henan Bebon Iron&Steel Co.,Ltd
address: XICHENG SCIENCE & TECHNOLOGY BUILDING HIGH-TECH DEVELOPMENT ZONE, ZHENGZHOU, CHINA
TEL: 0086-371-86151827
FAX: 0086-371-86011881
Email : [email protected]